Welding wire DIM L-1.4310
Description:
Material no.: 1.4310
W.-Nr.: 1.4310 X 10 CrNi18-8
DIN 10088-3
AISI 302
Characteristics:
The material DIM L-1.4310 is an austenitic steel that has a high chromium and nickel content and
has good polishability. A typical area of application for this stainless steel grade is industrial
Manufacture of springs. The material is well suited for welding and cold forming.
Please note that the magnetizability changes through cold forming.
Materials:
Identical and similar CrNi materials.
Analysis in %:
C |
Si |
Mn |
N |
Cr |
Mo |
Ni | Fe |
<0.15 |
2.0 |
2.0 |
0.1 |
16-19 |
0.8 |
6-9.5 | rest |
Mechanical properti es of pure weld metal:
pure weld metal | at room temperature |
Yield strength Rp0.2 MPa | 400 |
Tensile strength Rm MPa | 600 |
Elongation A (L0=5d0) % | 35 |
Impact energy KV J | 100 |
- Australia
- Germany
- Switzerland
- Austria
- Argentina
Welding wire DIM L-1.4310
Description:
Material no.: 1.4310
W.-Nr.: 1.4310 X 10 CrNi18-8
DIN 10088-3
AISI 302
Characteristics:
The material DIM L-1.4310 is an austenitic steel that has a high chromium and nickel content and
has good polishability. A typical area of application for this stainless steel grade is industrial
Manufacture of springs. The material is well suited for welding and cold forming.
Please note that the magnetizability changes through cold forming.
Materials:
Identical and similar CrNi materials.
Analysis in %:
C |
Si |
Mn |
N |
Cr |
Mo |
Ni | Fe |
<0.15 |
2.0 |
2.0 |
0.1 |
16-19 |
0.8 |
6-9.5 | rest |
Mechanical properti es of pure weld metal:
pure weld metal | at room temperature |
Yield strength Rp0.2 MPa | 400 |
Tensile strength Rm MPa | 600 |
Elongation A (L0=5d0) % | 35 |
Impact energy KV J | 100 |