LAWI-13-M
Welding wire LAWI 13 M
Description:
Cr-Mo-Mn-Si filler metal with highly lowered c-content. Including stabilizing elements to moderate hard carbide rims. Polishable, erodable, nitrable, etchable and heat treatable. Due to higher chrome content higher hardness and thus a bit darker than Lawi 14 M.
The weld is synchronous to the base metal regarding microstructure and treatment. Hardness 1-st layer approx. 390-450 HB.
Suitable for material nos. 1.1730, 1.2311, 1.2312, 1.2162, 1.2738 and similar.
Analysis in %:
C |
Al |
Cr |
Fe |
Mn |
Mo |
Si |
0.06 |
0.03 |
2.75 |
Rest |
0.95 |
1.0 |
0.6 |
The technical results are dependent on the extent of mingling to the basic materials
and also an indication of the process engineering.
- Australia
- Germany
- Denmark
- Switzerland
- Austria
- Argentina
Welding wire LAWI 13 M
Description:
Cr-Mo-Mn-Si filler metal with highly lowered c-content. Including stabilizing elements to moderate hard carbide rims. Polishable, erodable, nitrable, etchable and heat treatable. Due to higher chrome content higher hardness and thus a bit darker than Lawi 14 M.
The weld is synchronous to the base metal regarding microstructure and treatment. Hardness 1-st layer approx. 390-450 HB.
Suitable for material nos. 1.1730, 1.2311, 1.2312, 1.2162, 1.2738 and similar.
Analysis in %:
C |
Al |
Cr |
Fe |
Mn |
Mo |
Si |
0.06 |
0.03 |
2.75 |
Rest |
0.95 |
1.0 |
0.6 |
The technical results are dependent on the extent of mingling to the basic materials
and also an indication of the process engineering.