LAWI-28
Welding wire LAWI 28
Description:
Cr-Mn-Al-Ti universal filler metal for cold-cutling steels and tempering steels. The welding deposit is nitrable, crack- and abrasion resistant, induction and flame hardenable. Very suitable for closing edges of plastic blowing moulds. Hardness 1-st layer approx. 56-60 HRC can differ, depending on the extent of mingling. Hardenable up to approx. 62 HRC.
Analysis in %:
C |
Al |
Cr |
Fe |
Mn |
Si |
Ti |
1.20 |
0.50 |
2.0 |
Rest |
1.8 |
0.6 |
0.80 |
The technical results are dependent on the extent of mingling to the basic materials and also an indication of the process engineering.
- Australia
- Germany
- Denmark
- Switzerland
- Austria
- Argentina
Welding wire LAWI 28
Description:
Cr-Mn-Al-Ti universal filler metal for cold-cutling steels and tempering steels. The welding deposit is nitrable, crack- and abrasion resistant, induction and flame hardenable. Very suitable for closing edges of plastic blowing moulds. Hardness 1-st layer approx. 56-60 HRC can differ, depending on the extent of mingling. Hardenable up to approx. 62 HRC.
Analysis in %:
C |
Al |
Cr |
Fe |
Mn |
Si |
Ti |
1.20 |
0.50 |
2.0 |
Rest |
1.8 |
0.6 |
0.80 |
The technical results are dependent on the extent of mingling to the basic materials and also an indication of the process engineering.
- Australia
- Germany
- Denmark
- Switzerland
- Austria
- Argentina