LAWI-56
Welding wire LAWI 56
Description:
Cr-Mo-Mn filler metal special for the 17 % martensitic chrome-steels. Highly resistant to rust and wear. The welding deposit is polishable, erodable, nitrable, etchable and heat-treatable. Cannot be chromium-plated. For plastic- and blow molds.
The welding material is crack-free and harmonizes with the base materials in the melting zone.
Hardness 1-st layer approx. 50 - 58 HRC can differ, depending on the extent of mingling.
Suitable for materials No. 1.2083, 1.2316, 1.4115, 1.4120, STAVAX and similar steels.
Analysis in %:
|
C |
Cr |
Mn |
Mo |
Ni |
Si |
S |
P |
|
0.45 |
18 |
1.1 |
1.4 |
1.0 |
1.1 |
0.02 |
0.05 |
The technical results are dependent on the extent of mingling to the basic materials and also an indication of the process engineering.
- Australia
- Germany
- Denmark
- Switzerland
- Austria
- Argentina
Welding wire LAWI 56
Description:
Cr-Mo-Mn filler metal special for the 17 % martensitic chrome-steels. Highly resistant to rust and wear. The welding deposit is polishable, erodable, nitrable, etchable and heat-treatable. Cannot be chromium-plated. For plastic- and blow molds.
The welding material is crack-free and harmonizes with the base materials in the melting zone.
Hardness 1-st layer approx. 50 - 58 HRC can differ, depending on the extent of mingling.
Suitable for materials No. 1.2083, 1.2316, 1.4115, 1.4120, STAVAX and similar steels.
Analysis in %:
|
C |
Cr |
Mn |
Mo |
Ni |
Si |
S |
P |
|
0.45 |
18 |
1.1 |
1.4 |
1.0 |
1.1 |
0.02 |
0.05 |
The technical results are dependent on the extent of mingling to the basic materials and also an indication of the process engineering.