DIM-L-1.4351
Welding wire DIM L-1.4351
Description:
Material no.: 1.4351
DIN 8556: SG X3CrNi13-4
EN ISO 14343-A: G 13 4
EN ISO 14343-B: SS(410NiMo)
AWS A5.9: ER410NiMo (mod.)
Highly alloyed, non-corrosive
Characteristics:
Application in water turbine compressor construction (sea water power stations), rotors and steam power plant
construction. Resistant to water and steam. Excellent lubricity and conveying properties. Stainless and corrosion-
resistant as 13% Cu (Ni) steels. High resistance to vibration crack corrosion. Tough, wear-, erosion- and cavitation-
resistant.
Very good welding and flow behavior.
Materials:
1.4008 (GX7CrNiMo12-1), 1.4034 (X39Cr13), 1.4313 (X3CrNiMo13-4),
1.4317 (GX4CrNi13-4), 1.4351 (GX3CrNi13-4), 1.4407 (GX5CrNiMo13-4),
1.4414 (GX4CrNiMo13-4)
ACI Gr. CA 6 NM
ASTM A743 Gr. CA6NM
Analysis in %:
|
C |
Si |
Mn |
Cr |
Ni |
Mo |
||
|
0.01 |
0.65 |
0.7 |
12.2 |
4.8 |
0.5 |
Mechanical properti es of pure weld metal:
| pure weld metal | u* | a* |
| Tensile strength Rm MPa | 1250 | 890 (≥ 750) |
| Yield strengthRp0.2 MPa | 950 | 760 (≥ 500) |
| Elongati on A (L0=5d0) % | 12 | 17 (≥ 15) |
| Impact energy ISO-V KV J +20°C | -20°C | 36 | 80 |
u* untreated, welding state - protective gas Ar + 8-10% CO2
a* annealed, 580°C/8 h oven up to 300°C/air – protection gas Ar + 8-10% CO2
| pure weld metal | |
| Hardness HRC | 43 |
| Hardness HRC after cold hardening | 47 |
- Germany
- Denmark
- Switzerland
- Austria
- Argentina
Welding wire DIM L-1.4351
Description:
Material no.: 1.4351
DIN 8556: SG X3CrNi13-4
EN ISO 14343-A: G 13 4
EN ISO 14343-B: SS(410NiMo)
AWS A5.9: ER410NiMo (mod.)
Highly alloyed, non-corrosive
Characteristics:
Application in water turbine compressor construction (sea water power stations), rotors and steam power plant
construction. Resistant to water and steam. Excellent lubricity and conveying properties. Stainless and corrosion-
resistant as 13% Cu (Ni) steels. High resistance to vibration crack corrosion. Tough, wear-, erosion- and cavitation-
resistant.
Very good welding and flow behavior.
Materials:
1.4008 (GX7CrNiMo12-1), 1.4034 (X39Cr13), 1.4313 (X3CrNiMo13-4),
1.4317 (GX4CrNi13-4), 1.4351 (GX3CrNi13-4), 1.4407 (GX5CrNiMo13-4),
1.4414 (GX4CrNiMo13-4)
ACI Gr. CA 6 NM
ASTM A743 Gr. CA6NM
Analysis in %:
|
C |
Si |
Mn |
Cr |
Ni |
Mo |
||
|
0.01 |
0.65 |
0.7 |
12.2 |
4.8 |
0.5 |
Mechanical properti es of pure weld metal:
| pure weld metal | u* | a* |
| Tensile strength Rm MPa | 1250 | 890 (≥ 750) |
| Yield strengthRp0.2 MPa | 950 | 760 (≥ 500) |
| Elongati on A (L0=5d0) % | 12 | 17 (≥ 15) |
| Impact energy ISO-V KV J +20°C | -20°C | 36 | 80 |
u* untreated, welding state - protective gas Ar + 8-10% CO2
a* annealed, 580°C/8 h oven up to 300°C/air – protection gas Ar + 8-10% CO2
| pure weld metal | |
| Hardness HRC | 43 |
| Hardness HRC after cold hardening | 47 |