Welding wire DIM L-1.4519

 

Description:

Material no.: 1.4519

DIN 8556: SG X2CrNiMoCu20 25

EN ISO 14343-A: G Z20 25 5 Cu N L

EN ISO 14343-B: S S385

EN 12072: G Z20 25 5 Cu N L

AWS A5.9: ER385 (mod.)

Für high-corrosion CrNiMo-steels

 

Characteristics:

The weld metal is austenitic. Resistant to intercrystalline corrosion. Resistant in non-oxidizing bodies (up to 90%
sulfuric acid, phosphoric acid and organic acids).
Solid wire electrode for steels such as 1.4539 (904L) with an above-average high Mo-content and very high effective sum (PREN ≤ 45) of the weld material for the pitting potential (according to% Cr + 3.3 x% Mo + 30 x% N).
Resistant to chloride in solutions containing chloride. Scaling resistance up to 1000° C (air). Permissible temperature: -10° C to +350° C.
Special application in sulfur and phosphoric acid production, in the medical and pharmaceutical industry, in the
pulp industry and in flue gas desulphurization plants. Moreover, in the fertilizer industry, petrochemical sector,
fatty acid processing, acetic and formic acid production, seawater desalination, in pickling plants and heat exchangers, which are operated with sea or brackish water.
Resistant against crack corrosion in media containing chloride, high resistance to sulfuric, phosphoric, acetic and
formic acid, as well as sea and brackish water. The high Ni-content results in comparison with the conventional
18/8 CrNi welding products to have a very good resistance to stress corrosion cracking.
Due to the high overlay at Mo compared to 1.4539 or UNS N08904, the high rate of increase of Mo-alloyed CrNi
welding products can be compensated for.

 

Materials:

Same type high-Mo containing Cr-Ni steels1.4539 X1NiCrMoCu25-20-5,
1.4439 X2CrNiMoN17-13-5, 1.4537 X1CrNiMoCuN25-25-5
UNS N08904, S31726
Same and similar type CrNiMo-steels: 1.4505/06, 1.4529/31/36, 1.4585
Non-stabilized and stabilized austenitic CrNi steels: 1.4301/06, 1.4401/04/06/08, 1.4429, 1.4435/36, 1.4541,
1.4550/52, 1.4571/73, 1.4580/83

 

Analysis in %:

C

Si

Mn

Cr

Ni

Mo

N Cu PREN

≤ 0.02

0.7

4.7

20.0

25.4

6.2

0.12 1.5 ≥ 45.0

 

Mechanical properties of pure weld metal: 

pure weld metal u*
Tensile strength Rm MPa 650 (≥ 510)
Yield strengthRp0.2 MPa 410 (≥ 320)
Elongation A 5 (%) 39 (≥ 25)
Impact energy ISO-V KV J +20°C | -196°C 100 | (≥ 32)

 u*: untreated, welding state - protective gas Ar + 20% He + 0.5% CO2

Only available in following countries:
  • Germany
  • Switzerland
  • Austria
  • Argentina
Additional Informations
Additional Information:
Data sheet 988 KB
Query on the Item?
Do you have any questions on this item?
Your E-mail Adress
My Question:
Please retype the letters shown here
captcha
Description
Additional Informations
Query on the Item?

Welding wire DIM L-1.4519

 

Description:

Material no.: 1.4519

DIN 8556: SG X2CrNiMoCu20 25

EN ISO 14343-A: G Z20 25 5 Cu N L

EN ISO 14343-B: S S385

EN 12072: G Z20 25 5 Cu N L

AWS A5.9: ER385 (mod.)

Für high-corrosion CrNiMo-steels

 

Characteristics:

The weld metal is austenitic. Resistant to intercrystalline corrosion. Resistant in non-oxidizing bodies (up to 90%
sulfuric acid, phosphoric acid and organic acids).
Solid wire electrode for steels such as 1.4539 (904L) with an above-average high Mo-content and very high effective sum (PREN ≤ 45) of the weld material for the pitting potential (according to% Cr + 3.3 x% Mo + 30 x% N).
Resistant to chloride in solutions containing chloride. Scaling resistance up to 1000° C (air). Permissible temperature: -10° C to +350° C.
Special application in sulfur and phosphoric acid production, in the medical and pharmaceutical industry, in the
pulp industry and in flue gas desulphurization plants. Moreover, in the fertilizer industry, petrochemical sector,
fatty acid processing, acetic and formic acid production, seawater desalination, in pickling plants and heat exchangers, which are operated with sea or brackish water.
Resistant against crack corrosion in media containing chloride, high resistance to sulfuric, phosphoric, acetic and
formic acid, as well as sea and brackish water. The high Ni-content results in comparison with the conventional
18/8 CrNi welding products to have a very good resistance to stress corrosion cracking.
Due to the high overlay at Mo compared to 1.4539 or UNS N08904, the high rate of increase of Mo-alloyed CrNi
welding products can be compensated for.

 

Materials:

Same type high-Mo containing Cr-Ni steels1.4539 X1NiCrMoCu25-20-5,
1.4439 X2CrNiMoN17-13-5, 1.4537 X1CrNiMoCuN25-25-5
UNS N08904, S31726
Same and similar type CrNiMo-steels: 1.4505/06, 1.4529/31/36, 1.4585
Non-stabilized and stabilized austenitic CrNi steels: 1.4301/06, 1.4401/04/06/08, 1.4429, 1.4435/36, 1.4541,
1.4550/52, 1.4571/73, 1.4580/83

 

Analysis in %:

C

Si

Mn

Cr

Ni

Mo

N Cu PREN

≤ 0.02

0.7

4.7

20.0

25.4

6.2

0.12 1.5 ≥ 45.0

 

Mechanical properties of pure weld metal: 

pure weld metal u*
Tensile strength Rm MPa 650 (≥ 510)
Yield strengthRp0.2 MPa 410 (≥ 320)
Elongation A 5 (%) 39 (≥ 25)
Impact energy ISO-V KV J +20°C | -196°C 100 | (≥ 32)

 u*: untreated, welding state - protective gas Ar + 20% He + 0.5% CO2

Only available in following countries:
  • Germany
  • Switzerland
  • Austria
  • Argentina
Additional Information:
Data sheet 988 KB
Do you have any questions on this item?
Your E-mail Adress
My Question:
Please retype the letters shown here
captcha
* All prices are plus VAT | plus shipping costs | ALPHA LASER GmbH - Junkersstraße 16 - D-82178 Puchheim | © Shopsoftware CosmoShop