DIM-L-1.6356
Welding wire DIM L-1.6356
Description:
Material no.: 1.6356
EN/DIN 8555: W/MSG 3-GZ-350-T
EN 14700: S Z Fe5
AMS 6512: MIL-S-46850 (Grade 350)
Characteristics:
DIM L-1.6356 NiCo is a high-alloyed, artificially aged, highly tough and extremely wear resistant laser welding
wire for heavily stressed cold- and hot-working tools (co alloyed).
DIM L-1.6356 NiCo works crack preventing in case of momentary temperature deterrence and is therefore applied
on aluminum-dies as well as precautionary for hot crack repairs. The welding can be modified and reworked
easily by hand.
Due to the high heat resistance of DIM L-1.6356 NiCo, the material is also very suitable for repairs on glass molds.
DIM L-1.6356 NiCo brings excellent characteristics against wear, even though its original hardness only lies at
around 35 HRC. The warm operating process within the tool operation causes an outsourcing process. Here, the
weld metal hardens up to 54 HRC.
Further application areas are the crack-resistant, multi layered structure of contours on any type of tool steels
and applications of work areas of draw- and embossing tools as well as folding-press dies, which is due to the
high glide coefficient metal on metal.
Specific base materials:
Several warm- and cold working steels, GG and GGG cast materials.
Materials of same type: 1.2706 / 1.2709 / Böhler W720/21/22 / 1.6354 / 1.6358 (AMS 6512-6514) /
Thyrodur / Corrax.
Hardness of first layer: 35 HRC
After warm outsourcing process up to 54 HRC.
After warm outsourcing 4h at 480° C: 54 HRC / contant warmth: > 58 HRC.
After plasma nitriding, emergence of Ti-Nitrid layer of 980 – 1000 V.
Analysis in %:
C |
Mn |
Ni |
Mo |
Ti | Al | Fe |
0.02 |
4.0 |
18.0 |
4.0 |
1.6 | 0.1 | Remainder |
- Australia
- Germany
- Denmark
- Switzerland
- Austria
- Argentina
Welding wire DIM L-1.6356
Description:
Material no.: 1.6356
EN/DIN 8555: W/MSG 3-GZ-350-T
EN 14700: S Z Fe5
AMS 6512: MIL-S-46850 (Grade 350)
Characteristics:
DIM L-1.6356 NiCo is a high-alloyed, artificially aged, highly tough and extremely wear resistant laser welding
wire for heavily stressed cold- and hot-working tools (co alloyed).
DIM L-1.6356 NiCo works crack preventing in case of momentary temperature deterrence and is therefore applied
on aluminum-dies as well as precautionary for hot crack repairs. The welding can be modified and reworked
easily by hand.
Due to the high heat resistance of DIM L-1.6356 NiCo, the material is also very suitable for repairs on glass molds.
DIM L-1.6356 NiCo brings excellent characteristics against wear, even though its original hardness only lies at
around 35 HRC. The warm operating process within the tool operation causes an outsourcing process. Here, the
weld metal hardens up to 54 HRC.
Further application areas are the crack-resistant, multi layered structure of contours on any type of tool steels
and applications of work areas of draw- and embossing tools as well as folding-press dies, which is due to the
high glide coefficient metal on metal.
Specific base materials:
Several warm- and cold working steels, GG and GGG cast materials.
Materials of same type: 1.2706 / 1.2709 / Böhler W720/21/22 / 1.6354 / 1.6358 (AMS 6512-6514) /
Thyrodur / Corrax.
Hardness of first layer: 35 HRC
After warm outsourcing process up to 54 HRC.
After warm outsourcing 4h at 480° C: 54 HRC / contant warmth: > 58 HRC.
After plasma nitriding, emergence of Ti-Nitrid layer of 980 – 1000 V.
Analysis in %:
C |
Mn |
Ni |
Mo |
Ti | Al | Fe |
0.02 |
4.0 |
18.0 |
4.0 |
1.6 | 0.1 | Remainder |