Welding wire LAWI 12 M
Description:
Cr-Ni-Mo-Mn filler metal with a lowered c-content. Including stabilizing elements to moderate hard carbide rims. Hardenable up to the 2. layer, polishable, erodable, nitrable, etchable and heat treatable. For repairs of plastic and injection moulds color synchronous for 2-5% nickeliferous tool steels. The welding deposit is resistant to alternating temperatures.
Hardness 1-st layer approx. 360-420 HB.
Recommend for the material no. 1.2713, 1.2714, 1.2740, 1.2743, 1.2744, 1.2747, 1.2764, 1.2766, 1.2767 and similar steels
Analysis in %:
|
C |
Cr |
Fe |
Mn |
Mo |
Si |
V |
Su% |
|
0.25 |
1.45 |
Rest |
0.50 |
0.40 |
0.30 |
0.20 |
2.20 |
The technical results are dependent on the extent of mingling to the basic materials
and also a indication of the process engineering.
- Australia
- Germany
- Denmark
- Switzerland
- Austria
- Argentina
Welding wire LAWI 12 M
Description:
Cr-Ni-Mo-Mn filler metal with a lowered c-content. Including stabilizing elements to moderate hard carbide rims. Hardenable up to the 2. layer, polishable, erodable, nitrable, etchable and heat treatable. For repairs of plastic and injection moulds color synchronous for 2-5% nickeliferous tool steels. The welding deposit is resistant to alternating temperatures.
Hardness 1-st layer approx. 360-420 HB.
Recommend for the material no. 1.2713, 1.2714, 1.2740, 1.2743, 1.2744, 1.2747, 1.2764, 1.2766, 1.2767 and similar steels
Analysis in %:
|
C |
Cr |
Fe |
Mn |
Mo |
Si |
V |
Su% |
|
0.25 |
1.45 |
Rest |
0.50 |
0.40 |
0.30 |
0.20 |
2.20 |
The technical results are dependent on the extent of mingling to the basic materials
and also a indication of the process engineering.
- Australia
- Germany
- Denmark
- Switzerland
- Austria
- Argentina