LAWI-15-M
Welding wire LAWI 10 M
Description:
Cr-Mo-Mn filler metal with lowered carbon and silicon content. Cr-content is under 0,15 % and so it`s nearly free of chrome-carbon. Additional elements which reduce the development of carbides. The welding deposit is polishable, erodable, nitrable, etchable and heat treatable.
The laser welding is softer and lighter than LAWI 14 M.
Hardness 1- st layer approx. 300-360 HB.
Suitable for material no.: 1.2311, 1.2312, 1.2162, 1.2738 and similar.
Analysis in %:
|
C |
Al |
Cr |
Cu |
Fe |
Mn |
Mo |
Si |
Ni |
Su% |
|
0.12 |
0.03 |
<0.12 |
0.17 |
Rest |
1.1 |
0.5 |
0.7 |
<0.12 |
0.45 |
The technical results are dependent on the extent of mingling to the basic materials
and also an indication of the process engineering.
- Germany
- Denmark
- Switzerland
- Austria
- Argentina
Welding wire LAWI 10 M
Description:
Cr-Mo-Mn filler metal with lowered carbon and silicon content. Cr-content is under 0,15 % and so it`s nearly free of chrome-carbon. Additional elements which reduce the development of carbides. The welding deposit is polishable, erodable, nitrable, etchable and heat treatable.
The laser welding is softer and lighter than LAWI 14 M.
Hardness 1- st layer approx. 300-360 HB.
Suitable for material no.: 1.2311, 1.2312, 1.2162, 1.2738 and similar.
Analysis in %:
|
C |
Al |
Cr |
Cu |
Fe |
Mn |
Mo |
Si |
Ni |
Su% |
|
0.12 |
0.03 |
<0.12 |
0.17 |
Rest |
1.1 |
0.5 |
0.7 |
<0.12 |
0.45 |
The technical results are dependent on the extent of mingling to the basic materials
and also an indication of the process engineering.