LAWI-30
Welding wire LAWI 30
Description:
Cr-Mn-Mo-V-W filler metal with extreme tough-hardened and wear resistant properties.
For cold work steels with approx. 5 % chromium. Crack resistant and hardenable. Edge-stable. The welding deposit is nitrable, erodable, chromium-platable and heat treatable. Hardness 1-st layer approx. 56-60 HRC can differ, depending on the extent of mingling. Hardenable up to approx. 62 HRC.
Analysis in %:
C |
S |
Cr |
Fe |
Mn |
Mo |
Ni |
Ti |
V |
W |
0.35 |
0.30 |
6.20 |
Rest |
1.0 |
2.0 |
0.5 |
0.25 |
0.60 |
0.80 |
The technical results are dependent on the extent of mingling to the basic materials and also an indication of the process engineering.
- Australia
- Germany
- Switzerland
- Austria
- Argentina
Welding wire LAWI 30
Description:
Cr-Mn-Mo-V-W filler metal with extreme tough-hardened and wear resistant properties.
For cold work steels with approx. 5 % chromium. Crack resistant and hardenable. Edge-stable. The welding deposit is nitrable, erodable, chromium-platable and heat treatable. Hardness 1-st layer approx. 56-60 HRC can differ, depending on the extent of mingling. Hardenable up to approx. 62 HRC.
Analysis in %:
C |
S |
Cr |
Fe |
Mn |
Mo |
Ni |
Ti |
V |
W |
0.35 |
0.30 |
6.20 |
Rest |
1.0 |
2.0 |
0.5 |
0.25 |
0.60 |
0.80 |
The technical results are dependent on the extent of mingling to the basic materials and also an indication of the process engineering.
- Australia
- Germany
- Switzerland
- Austria
- Argentina