LAWI-32
Welding wire LAWI 32
Description:
Cr-Mn-Si-V filler metal with elements for structure stabilization. The welding deposit is similar to the 12% chromium-cold cutting steels. Can not be chromium-plated however nitrable and erodable. Hardness 1-st layer approx. 58-60 HRC can differ, depending on the extent of mingling. Hardenable up to approx. 62 HRC.
For materials: 1.2379, 1.2080, 1.2436, 1.2601 and similar steels.
Analysis in %:
|
C |
Cr |
Fe |
Mn |
Si |
V |
|
0.45 |
9.0 |
Rest |
0.35 |
2.90 |
0.50 |
The technical results are dependent on the extent of mingling to the basic materials and also an indication of the process engineering.
- Australia
- Germany
- Switzerland
- Austria
- Argentina
Welding wire LAWI 32
Description:
Cr-Mn-Si-V filler metal with elements for structure stabilization. The welding deposit is similar to the 12% chromium-cold cutting steels. Can not be chromium-plated however nitrable and erodable. Hardness 1-st layer approx. 58-60 HRC can differ, depending on the extent of mingling. Hardenable up to approx. 62 HRC.
For materials: 1.2379, 1.2080, 1.2436, 1.2601 and similar steels.
Analysis in %:
|
C |
Cr |
Fe |
Mn |
Si |
V |
|
0.45 |
9.0 |
Rest |
0.35 |
2.90 |
0.50 |
The technical results are dependent on the extent of mingling to the basic materials and also an indication of the process engineering.
- Australia
- Germany
- Switzerland
- Austria
- Argentina