LAWI-62-EROD
Schweißdraht LAWI 62 EROD
Beschreibung:
Martensitic Cr filler metal with lowered C-content and added stabilizing elements.
Especially developed for repairs of GRP plastic injection and blow molded plastic, as well as for their inserts which are to be eroded after welding. Transitions and differences in colour are no longer visible if used properly. The welding deposit is rust- and wear-resistant, however cannot be chromium-plated!
Hardness 1-st layer approx. 45-55 HRC, depending on the extent of mingling and diameter of the wire (energy). Follow-up Hardenable up to approx. 60 HRC.
Richtanalyse in %:
|
C |
Cr |
Fe |
Mn |
Mo |
Ni |
Si |
V |
W |
Su% |
|
0.10 |
13.5 |
Rest |
0.70 |
1.50 |
<1.0 |
0.60 |
0.45 |
0.50 |
<1.0 |
Die technischen Ergebniswerte sind von der Aufmischung zu den Grundwerkstoffen, sowie als Hinweis verfahrensabhängig, je nach Schweiß-Parametern und Drahtdurchmesser.
- Australia
- Germany
- Switzerland
- Austria
- Argentina
Schweißdraht LAWI 62 EROD
Beschreibung:
Martensitic Cr filler metal with lowered C-content and added stabilizing elements.
Especially developed for repairs of GRP plastic injection and blow molded plastic, as well as for their inserts which are to be eroded after welding. Transitions and differences in colour are no longer visible if used properly. The welding deposit is rust- and wear-resistant, however cannot be chromium-plated!
Hardness 1-st layer approx. 45-55 HRC, depending on the extent of mingling and diameter of the wire (energy). Follow-up Hardenable up to approx. 60 HRC.
Richtanalyse in %:
|
C |
Cr |
Fe |
Mn |
Mo |
Ni |
Si |
V |
W |
Su% |
|
0.10 |
13.5 |
Rest |
0.70 |
1.50 |
<1.0 |
0.60 |
0.45 |
0.50 |
<1.0 |
Die technischen Ergebniswerte sind von der Aufmischung zu den Grundwerkstoffen, sowie als Hinweis verfahrensabhängig, je nach Schweiß-Parametern und Drahtdurchmesser.