LAWI-36
Welding wire LAWI 36
Description:
Special steel alloy, high-temperature resistant. Resistant to abrasion and oxidation under high temperatures. Martensitic welding deposit is crack resistant in warm-cold reactions. The welding deposit is resistant to pressure, impact and displacement and has stable edges. Hardness increase of the welding deposit at maximum 54 HRC after thermal treatment (4 h to 490 degrees). Good machinability but cannot be chromium plated.
Analysis in %:
C |
Al |
Co |
Cr |
Fe |
Mn |
Mo |
Ni |
Si |
V |
0.02 |
0.25 |
14.5 |
2.00 |
Rest |
0.20 |
4.70 |
19.30 |
0.20 |
0.40 |
The technical results are dependent on the extent of mingling to the basic materials
and also an indication of the process engineering.
- Australia
- Germany
- Denmark
- Switzerland
- Austria
- Argentina
Welding wire LAWI 36
Description:
Special steel alloy, high-temperature resistant. Resistant to abrasion and oxidation under high temperatures. Martensitic welding deposit is crack resistant in warm-cold reactions. The welding deposit is resistant to pressure, impact and displacement and has stable edges. Hardness increase of the welding deposit at maximum 54 HRC after thermal treatment (4 h to 490 degrees). Good machinability but cannot be chromium plated.
Analysis in %:
C |
Al |
Co |
Cr |
Fe |
Mn |
Mo |
Ni |
Si |
V |
0.02 |
0.25 |
14.5 |
2.00 |
Rest |
0.20 |
4.70 |
19.30 |
0.20 |
0.40 |
The technical results are dependent on the extent of mingling to the basic materials
and also an indication of the process engineering.